PETG-GF

Eryone PETG-GF filament is an enhanced PETG material that offers excellent flow
properties and ease of printing, along with low odor and outstanding chemical
resistance. Parts printed with this material are not only strong and durable but also
exhibit excellent dimensional stability, featuring a fine matte and frosted texture on the
surface. It is particularly suitable for manufacturing structural components or outdoor
models that require high impact resistance and durability against drops. It is important
to note that this material contains 10% glass fiber

Part I: Suggests Printing Parameters

Parameter	Set up
Nozzle temperature	250-280 ℃
Bed temperature	60-70℃
Bed material	glass, PEI, spring steel plate
Bottom printing temperature	250℃-280℃
Sealed printing	closed printing
Printing speed	30-150mm/s
Drying conditions	60℃-70℃，4-8H

Part II: Physical Properties of Materials

Property	Testing Method	Unit	Typical Value
Density(g/cm³ at 21.5 ° C）	ASTM D792 (ISO 1183, GB/T 1033)	g/cm³	1.33
Vicat Softening Temperature(° C)	ASTM D1525 (ISO 306 GB/T 1633)	℃	/
Heat distortion temperature(° C)	ASTM D648 1.8MPa 0.45MPa	℃	80
Glass transition temperature (° C)	DSC, 10 ° C/min	℃	75
Melt Index(g/10 min)	220 ° C, 10kg 240 ° C, 2.16 kg	g/10min	10

Part III: Mechanical Properties of Printed Samples

Property	Test conditions	Test standards	unit	Typical Value
Tensile strength X-Y	50mm/min	GB/T 1040.4	MPa	53.6
Elastic modulus X-Y	50mm/min	GB/T 1040.1-2006	MPa	2334.5
Elongation at break X-Y	50mm/min	GB/T 1040.4	%	1.9
Tensile strength X-Z	50mm/min	GB/T 1843	MPa	25.1
Elastic modulus X-Z	50mm/min	GB/T 1040.1-2006	MPa	2109.7
Elongation at break X-Z	50mm/min	GB/T 1040.4	%	1.7
Bending strength	2mm/min	GB/T 9341	MPa	78.5
Bending modulus	2mm/min	GB/T 9341	MPa	3027.5
Charpy Impact strenght	2.75J	GB/T 1843	kJ/m2	3.9

Note: All splines are printed under the following conditions: printing temperature=240 ° C, printing speed=80mm/s, base
plate 60 ° C, filling=100%, nozzle diameter=0.4mm

Disclaimers
The values given in this data table are for reference and comparison only. They should not
be used for design specifications or quality control. The actual value may vary depending on
the printing conditions. The final performance of printed components depends not only on the
material, but also on the component design, environmental conditions, printing conditions, and so on. Product specifications are subject to change without prior notice

PETG-GF

Part I: Suggests Printing Parameters

Part II: Physical Properties of Materials

Part III: Mechanical Properties of Printed Samples

Note: All splines are printed under the following conditions: printing temperature=240 ° C, printing speed=80mm/s, baseplate 60 ° C, filling=100%, nozzle diameter=0.4mm

Note: All splines are printed under the following conditions: printing temperature=240 ° C, printing speed=80mm/s, base
plate 60 ° C, filling=100%, nozzle diameter=0.4mm

CF & GF

PLA Carbon Fiber Filament - 1.75mm±0.03mm (1kg)

Nylon & Nylon-CF&GF(PA6 & PA12) Filament - 1.75mm±0.03mm (1kg)

PP & PP-CF Filament - 1.75mm±0.03mm (900g)

PETG Fiberglass Filament - 1.75mm±0.03mm (1kg)