ERYONE High speed Triple-Color Silk PLA IS COMING！

ERYONE Triple-Color Silk PLA Filament for 3D Printers,1kg (2.2LBS)/Spool 1.75mm,Accuracy +/- 0.03 mm

Why choose ERYONE for your 3D Printing Needs?

ERYONE focus on 3d printing filament research and development over 6 years! We have Much more experience of 3d printing filament so that offer best products and services.Our products cover almost all types of filament.Such as PLA filaments: PLA;PLA+;Matte PLA;Silk PLA;Ultra Silk PLA;Galaxy PLA;Rainbow PLA;Glow in the dark PLA;Carbon fiber PLA;Scented PLA;Wood PLA;Marble PLA. PETG Filaments: PETG;Galaxy PETG;Carbon fiber PETG. TPU Filaments: TPU;Rainbow TPU. ABS;ASA;Nylon etc. Of course we will keep to update and release new all the way!

Triple-Color PLA Features :

3 independent colors in one strand of filament
Silky, Glossy and Gorgeous 3 color change effect on 3 sides of prints offers you stunning visual enjoyment
High Dimensional Accuracy: 1.75mm, tolerance +/-0.03mm.
Neatly Winding, High Quality, No bubble or dust with vacuum storage bags inside
Compatible with most commonly used 3d printers

Technical Specification :

Filament Diameter: 1.75mm
Tolerance: ±0.03mm
Printing Temperature:190°C-220°C
Heated Bed Temperature: 60-70℃
Printing Speed:30-100mm/s

Part I:Suggests Printing Parameters

Parameter	Set up
Nozzle temperature	190℃-220℃
Bed temperature	55-70℃
Bed materia	glass, PEI, spring steel plate
Bottom printing temperature	190℃-220℃
Sealed printing	supports open printing, and the sealing effect is better if it is sealed
Printing speed	30-100mm/s
Drying conditions	55℃，8H

Part II:Physical Properties of Materials

Property	Testing Method	Unit	Typical Value
Density(g/cm³ at 21.5 ° C）	ASTM D792 (ISO 1183, GB/T 1033)	g/cm³	1.32
Vicat Softening Temperature(° C)	ASTM D1525 (ISO 306 GB/T 1633)	℃	56
Heat distortion temperature(° C)	ASTM D648 1.8MPa 0.45MPa	℃	53
Glass transition temperature (° C)	DSC, 10 ° C/min	℃	63
Melt Index(g/10 min)	220 ° C, 10kg 240 ° C, 2.16 kg	g/10min	20.5±1.5

Part III:Mechanical Properties of Printed Samples

Property	Test conditions	Test standards	unit	Typical Value
Tensile strength X-Y	50mm/min	GB/T 1040.4	MPa	49.8
Elastic modulus X-Y	50mm/min	GB/T 1040.1-2006	MPa	1724.9
Elongation at break X-Y	50mm/min	GB/T 1040.4	%	1.7
Tensile strength X-Z	50mm/min	GB/T 1843	MPa	11
Elastic modulus X-Z	50mm/min	GB/T 1040.1-2006	MPa	1653.5
Elongation at break X-Z	50mm/min	GB/T 1040.4	%	1.1
Bending strength	2mm/min	GB/T 9341	MPa	66.7
Bending modulus	2mm/min	GB/T 9341	MPa	2315.5
Charpy Impact strenght	2.75J	GB/T 1043.1-2008	kJ/m2	7.5

Warmly Note :

- If the consumables are not used for a long time, please keep them in a cool (temperature lower than 32℃) and dry environment (humidity lower than 40%) in time.

- Use a soft cloth to clean the nozzles before and after printing to avoid residual consumables from affecting the printer.

- If there is a problem of material blocking, please check whether the feeder spring is too loose to cause the filament to slip, and too tight to cause the filament to be damaged by the gear.

- The interlayer adhesion of silk consumables is weak. If the printed product is relatively thin, it will be easily torn laterally after being stressed. The hygroscopicity of silk consumables is stronger than that of standard PLA, so attention should be paid to sealing and drying.

- The Triple-Color pla cross is more obvious, the reasons as below:

Winding, here is a small roll of consumables, and its winding is not uniform, which is also an important reason for the three-color cross.
The more colors of the same section, the smaller the proportion of each color, so the probability of color crossing will be greater.

Summer Sale: Save 55% on Tri-Color and Dual-Color filaments! Use code 'MultiColorSale'.

PLA Silk Tri-color

PLA Silk Triple-Color Filament - 1.75mm±0.03mm (1kg)

PLA Silk High-Speed Triple-Color Filament - 1.75mm±0.03mm (1kg)