Standard PP

Eryone Standard PP filament is a material with excellent chemical resistance and
mechanical properties, showcasing good flexibility, making it ideal for applications such as
handles, lockable containers, and bottles for holding chemicals. This material is a tough, semirigid thermoplastic with outstanding heat resistance, electrical insulation, and wear resistance. During the printing process, it is recommended to apply specialized PP printing glue on the
heated bed to ensure optimal results.

Part I:Suggests Printing Parameters

Parameter	Set up
Nozzle temperature	220-240 ℃
Bed temperature	60-80℃
Bed materia	glass, PEI, spring steel plate
Bottom printing temperature	220-240 ℃
Sealed printing	closed printing
Printing speed	30-100mm/s
Drying conditions	50-60℃, 8h

Part II: Physical Properties of Materials

Property	Testing Method	Unit	Typical Value
Density(g/cm³ at 21.5 ° C）	ASTM D792 (ISO 1183, GB/T 1033)	g/cm³	0.95
Vicat Softening Temperature(° C)	ASTM D1525 (ISO 306 GB/T 1633)	℃	55-63
Heat distortion temperature(° C)	ASTM D648 1.8MPa 0.45MPa	℃	55
Melt Index(g/10 min)	220 ° C, 10kg 240 ° C, 2.16 kg	g/10min	12-15

Part III: Mechanical Properties of Printed Samples

Property	Test conditions	Test standards	unit	Typical Value
Tensile strength X-Y	50mm/min	GB/T 1040.4	MPa	23-29
Elastic modulus X-Y	50mm/min	GB/T 1040.1-2006	MPa	35-45
Elongation at break X-Y	50mm/min	GB/T 1040.4	%	＞80

Note: All splines are printed under the following conditions: printing temperature=230 ° C, printing speed=80mm/s, base plate 80 ° C, filling=100%, nozzle diameter=0.4mm

PP Carbon-Fiber

PP & PP-CF Filament - 1.75mm±0.03mm (900g)